| POLYMER CLASS | Polyhaloolefins |
| COMMON NAMES | Poly(vinyl fluoride), Tedlar® |
| STRUCTURE BASED NAME | Poly(fluoroethylene) |
| ACRONYMS | PVF |
| CAS # | 24981-14-4 |
| CurlySMILES | C{-}(F)C{n+} |
| CAS # | 75-02-5 |
| COMMON NAMES | Vinyl fluoride |
| SMILES | FC=C |
| Std. InChI | 1S/C2H3F/c1-2-3/h2H,1H2 |
| Std. InChIKey | XUCNUKMRBVNAPB-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | 33.3 - 36.0 | 34.4 |
| Density ρ | g mL-1 | 1.28 - 1.38 | 1.34 |
| Solubility Parameter δ | MPa1/2 | 14.6 - 16.3 | 15.7 |
| Molar Cohesive Energy Ecoh | J mol-1 | 7900 - 9800 | 8500 |
| Glass Transition Temperature Tg | K | 253 314 - 337 | 253 326 |
| Molar Heat Capacity Cp | J (mol K)-1 | 59.5 (s) | |
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none | 1.46 |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 46.04 | |
| Van-der-Waals Volume VvW | mL mol-1 | 22.45 | |
| Molar Volume Vm | mL mol-1 | 36.3 - 37.7 | 36.9 |
| Density ρ | g mL-1 | 1.25 - 1.27 | 1.26 |
| Solubility Parameter δ | MPa1/2 | 14.6 - 15.8 | 15.1 |
| Molar Cohesive Energy Ecoh | J mol-1 | 7700 - 9200 | 8500 |
| Glass Transition Temperature Tg | K | 269, 338 | |
| Molar Heat Capacity Cp | J (mol K)-1 | 52
- 62 72 - 79 | 59 (s) 75 (l,r) |
| Entanglement Molecular Weight Me | g mol-1 | 1400 - 1950 | 1650 |
| Index of Refraction n | none | 1.40 - 1.42 | 1.41 |