| POLYMER CLASS | Polyacrylates |
| COMMON NAMES | Poly(tert-butyl acrylate) |
| STRUCTURE BASED NAME | Poly(tert-butyl propenoate) |
| ACRONYMS | 25232-27-3 |
| CAS # | |
| CurlySMILES | C{-}C{n+}(C(=O)OC(C)(C)C) |
| CAS # | 1663-39-4 |
| COMMON NAMES | tert-Butyl acrylate |
| SMILES | C=CC(=O)OC(C)(C)C |
| Std. InChI | 1S/C9H16O2/c1-5-9(10)11-8(4)6-7(2)3/h5,7-8H,1,6H2,2-4H3 |
| Std. InChIKey | ISXSCDLOGDJUNJ-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | 128.2 | |
| Density ρ | g mL-1 | 1.00 | |
| Solubility Parameter δ | MPa1/2 | ||
| Molar Cohesive Energy Ecoh | J mol-1 | ||
| Glass Transition Temperature Tg | K | 346, 380, 304 - 316 | 311 |
| Molar Heat Capacity Cp | J (mol K)-1 | ||
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 128.17 | |
| Van-der-Waals Volume VvW | mL mol-1 | 76.76 | |
| Molar Volume Vm | mL mol-1 | 117.0 - 121.6 | 118.6 |
| Density ρ | g mL-1 | 1.05 - 1.10 | 1.08 |
| Solubility Parameter δ | MPa1/2 | 17.4 - 17.8 | 17.7 |
| Molar Cohesive Energy Ecoh | J mol-1 | 36700 - 37700 | 37100 |
| Glass Transition Temperature Tg | K | 295 - 332 | 314 |
| Molar Heat Capacity Cp | J (mol K)-1 | 181 - 200 | 188 |
| Entanglement Molecular Weight Me | g mol-1 | 16800 - 17200 | 17000 |
| Index of Refraction n | none | 1.47 - 1.49 | 1.48 |