POLYMER CLASS | Polyacrylates |
COMMON NAMES | Poly(hexyl acrylate) |
STRUCTURE BASED NAME | Poly(hexyl propenoate) |
ACRONYMS | |
CAS # | 27103-47-5 |
CurlySMILES | C{-}C{n+}(C(=O)OCCCCCC) |
CAS # | 219-698-5 |
COMMON NAMES | Hexyl acrylate |
SMILES | CCCCCCOC(=O)C=C |
Std. InChI | InChI=1S/C9H16O2/c1-3-5-6-7-8-11-9(10)4-2/h4H,2-3,5-8H2,1H3 |
Std. InChIKey | LNMQRPPRQDGUDR-UHFFFAOYSA-N |
STRUCTURE |
![]() |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molar Volume Vm | mL mol-1 | 151.5* | |
Density ρ | g mL-1 | 1.03* | |
Solubility Parameter δ | MPa1/2 | ||
Molar Cohesive Energy Ecoh | J mol-1 | ||
Glass Transition Temperature Tg | K | 192 - 216 | 215 |
Molar Heat Capacity Cp | J (mol K)-1 | ||
Entanglement Molecular Weight Me | g mol-1 | ||
Index of Refraction n | none |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molecular Weight of Repeat unit | g mol-1 | 156.23 | |
Van-der-Waals Volume VvW | mL mol-1 | 97.3 | |
Molar Volume Vm | mL mol-1 | 148.1 - 153.9 | 150.7 |
Density ρ | g mL-1 | 1.01 - 1.05 | 1.04 |
Solubility Parameter δ | MPa1/2 | 17.7 - 18.6 | 18.1 |
Molar Cohesive Energy Ecoh | J mol-1 | 47100 - 49900 | 49300 |
Glass Transition Temperature Tg | K | 214 - 227 | 219 |
Molar Heat Capacity Cp | J (mol K)-1 | 300.5 - 311.9 | 306.1 |
Entanglement Molecular Weight Me | g mol-1 | 27800 - 26600 | 27200 |
Index of Refraction n | none | 1.47 - 1.49 | 1.48 |