| POLYMER CLASS | Polyacrylates |
| COMMON NAMES | Poly(cyclohexyl acrylate) |
| STRUCTURE BASED NAME | Poly(cyclohexyl propenoate), Poly[1-(cyclohexyloxycarbonyl)ethylene] |
| ACRONYMS | |
| CAS # | 27458-65-7 |
| CurlySMILES | C{-}C{n+}(C(=O)OC1CCCCC1) |
| CAS # | 125658-21-1 |
| COMMON NAMES | Cyclohexyl acrylate |
| SMILES | C=CC(=O)OC1CCCCC1 |
| Std. InChI | 1S/C9H14O2/c1-2-9(10)11-8-6-4-3-5-7-8/h2,8H,1,3-7H2 |
| Std. InChIKey | KBLWLMPSVYBVDK-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | 142.7 | |
| Density ρ | g mL-1 | 1.08 | |
| Solubility Parameter δ | MPa1/2 | ||
| Molar Cohesive Energy Ecoh | J mol-1 | ||
| Glass Transition Temperature Tg | K | 285 - 292 | 289 |
| Molar Heat Capacity Cp | J (mol K)-1 | 207 (s) 274 (l,r) | |
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 154.21 | |
| Van-der-Waals Volume VvW | mL mol-1 | 90.05 | |
| Molar Volume Vm | mL mol-1 | 135.5 - 136.8 | 136.2 |
| Density ρ | g mL-1 | 1.13 - 1.14 | 1.13 |
| Solubility Parameter δ | MPa1/2 | 18.8 - 19.1 | 19.0 |
| Molar Cohesive Energy Ecoh | J mol-1 | 48000 - 49500 | 49000 |
| Glass Transition Temperature Tg | K | 283 - 288 | 286 |
| Molar Heat Capacity Cp | J (mol K)-1 | 191 - 211 268 - 287 | 193 (s) 269 (l,r) |
| Entanglement Molecular Weight Me | g mol-1 | 17000 - 27000 | 22000 |
| Index of Refraction n | none | 1.49 - 1.51 | 1.51 |