| POLYMER CLASS | Polyacrylates |
| COMMON NAMES | Poly(butyl acrylate) |
| STRUCTURE BASED NAME | Poly(butyl propenoate) |
| ACRONYMS | |
| CAS # | 9003-49-0 |
| CurlySMILES | C{-}C{n+}(C(=O)OCCCC) |
| CAS # | 112790-39-3 |
| COMMON NAMES | Butyl acrylate |
| SMILES | CCCCOC(=O)C=C |
| Std. InChI | 1S/C7H12O2/c1-3-5-6-9-7(8)4-2/h4H,2-3,5-6H2,1H3 |
| Std. InChIKey | CQEYYJKEWSMYFG-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | 117.6 - 119.8 | 118.7 |
| Density ρ | g mL-1 | 1.07 - 1.09 | 1.08 |
| Solubility Parameter δ | MPa1/2 | 18.0 - 20.4 | 18.5 |
| Molar Cohesive Energy Ecoh | J mol-1 | 38500 - 49300 | 40400 |
| Glass Transition Temperature Tg | K | 218 - 224 | 220 |
| Molar Heat Capacity Cp | J (mol K)-1 | 229 - 233 | 231 |
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none | 1.46 - 1.47 | 1.47 |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 128.17 | |
| Van-der-Waals Volume VvW | mL mol-1 | 76.76 | |
| Molar Volume Vm | mL mol-1 | 117.0 - 120.9 | 118.4 |
| Density ρ | g mL-1 | 1.06 - 1.10 | 1.08 |
| Solubility Parameter δ | MPa1/2 | 18.1 - 19.0 | 18.4 |
| Molar Cohesive Energy Ecoh | J mol-1 | 38200 - 42200 | 40300 |
| Glass Transition Temperature Tg | K | 229 - 233 | 229 |
| Molar Heat Capacity Cp | J (mol K)-1 | 239 - 248 | 246 |
| Entanglement Molecular Weight Me | g mol-1 | 17000 - 19000 | 18000 |
| Index of Refraction n | none | 1.46 - 1.49 | 1.48 |