| POLYMER CLASS | Epoxy Resin |
| COMMON NAMES | Poly(bisphenol-A diglycidyl ether- alt - ethylenediamine), DGEBA-Edamine Epoxy |
| STRUCTURE BASED NAME | Poly(iminoethyleneimino-2-hydroxytrimethyleneoxy-1,4-phenylene-(dimethylmethylene)-1,4-phenylene-oxy-2-hydroxtrimethylene) |
| ACRONYMS | |
| CAS # | |
| CurlySMILES | C{-}C(O)COc1ccc(cc1)C(C)(C)c2ccc(cc2)OCC(O)CNCCN{n+} |
| CAS # | 116161-20-7.107-15-3 |
| COMMON NAMES | Bisphenol A diglycidyl ether + Ethylenediamine |
| SMILES | CC(c1ccc(cc1)OCC1OC1)(c1ccc(cc1)OCC1OC1)C.NCCN |
| Std. InChI | 1S/C21H24O4/c1-21(2,15-3-7-17(8-4-15)22-11-19-13-24-19)16-5-9-18(10-6-16)23-12-20-14-25-20/h3-10,19-20H,11-14H2,1-2H3.1S/C2H8N2/c3-1-2-4/h1-4H2 |
| Std. InChIKey | LCFVJGUPQDGYKZ-UHFFFAOYSA-N.PIICEJLVQHRZGT-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | ||
| Density ρ | g mL-1 | ||
| Solubility Parameter δ | MPa1/2 | 22.4 | |
| Molar Cohesive Energy Ecoh | J mol-1 | 176800 | |
| Glass Transition Temperature Tg | K | 410 | |
| Molar Heat Capacity Cp | J (mol K)-1 | ||
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 400.52 | |
| Van-der-Waals Volume VvW | mL mol-1 | 223.77 | |
| Molar Volume Vm | mL mol-1 | 349.1 - 356.0 | 352.5 |
| Density ρ | g mL-1 | 1.13 - 1.15 | 1.14 |
| Solubility Parameter δ | MPa1/2 | 22.1 - 22.3 | 22.2 |
| Molar Cohesive Energy Ecoh | J mol-1 | 172300 - 176000 | 174100 |
| Glass Transition Temperature Tg | K | 394 - 409 | 409 |
| Molar Heat Capacity Cp | J (mol K)-1 | 494 - 524 | 508 |
| Entanglement Molecular Weight Me | g mol-1 | 1600 - 2100 | 1900 |
| Index of Refraction n | none | 1.55 - 1.62 | 1.57 |