| POLYMER CLASS | Epoxy Resin |
| COMMON NAMES | Poly(bisphenol-A diglycidyl ether-alt-1,6-diamino hexane), DGEBA-Octanediamine Epoxy, Poly(bis-A diglycidyl ether- alt - octamethylenediamine) |
| STRUCTURE BASED NAME | Poly(iminooctamethyleneimino-2-hydroxytrimethyleneoxy-1,4-phenylene-(dimethylmethylene)-1,4-phenylene-oxy-2-hydroxtrimethylene) |
| ACRONYMS | |
| CAS # | |
| CurlySMILES | C{-}C(O)COc1ccc(cc1)C(C)(C)c2ccc(cc2)OCC(O)CNCCCCCCCCN{n+} |
| CAS # | 1675-54-3.231-522-9 |
| COMMON NAMES | Bisphenol A diglycidyl ether + 1,8-Diaminooctane (Octamethylenediamine) |
| SMILES | CC(c1ccc(cc1)OCC1OC1)(c1ccc(cc1)OCC1OC1)C.NCCCCCCCCN |
| Std. InChI | 1S/C21H24O4/c1-21(2,15-3-7-17(8-4-15)22-11-19-13-24-19)16-5-9-18(10-6-16)23-12-20-14-25-20/h3-10,19-20H,11-14H2,1-2H3.1S/C8H20N2/c9-7-5-3-1-2-4-6-8-10/h1-10H2 |
| Std. InChIKey | LCFVJGUPQDGYKZ-UHFFFAOYSA-N.PWGJDPKCLMLPJW-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | ||
| Density ρ | g mL-1 | ||
| Solubility Parameter δ | MPa1/2 | 20.7 | |
| Molar Cohesive Energy Ecoh | J mol-1 | 191600 | |
| Glass Transition Temperature Tg | K | 376 | |
| Molar Heat Capacity Cp | J (mol K)-1 | ||
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 484.68 | |
| Van-der-Waals Volume VvW | mL mol-1 | 264.9 | |
| Molar Volume Vm | mL mol-1 | 448 - 449 | 449 |
| Density ρ | g mL-1 | 1.08 | |
| Solubility Parameter δ | MPa1/2 | 21.0 - 21.2 | 21.1 |
| Molar Cohesive Energy Ecoh | J mol-1 | 198000 - 202000 | 199700 |
| Glass Transition Temperature Tg | K | 378 | |
| Molar Heat Capacity Cp | J (mol K)-1 | 635 - 673.5 | 655 |
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |