| POLYMER CLASS | Polyacrylate |
| COMMON NAMES | Poly(4-chlorophenyl acrylate) |
| STRUCTURE BASED NAME | Poly(4-chlorophenyl propenoate) |
| ACRONYMS | |
| CAS # | |
| CurlySMILES | C{-}C{n+}(C(=O)Oc1ccc(cc1)Cl) |
| CAS # | 13633-87-9 |
| COMMON NAMES | Para-chlorophenyl acrylate |
| SMILES | C=CC(=O)Oc1ccc(cc1)Cl |
| Std. InChI | 1S/C9H7ClO2/c1-2-9(11)12-8-5-3-7(10)4-6-8/h2-6H,1H2 |
| Std. InChIKey | IGHDIBHFCIOXGK-UHFFFAOYSA-N |
| STRUCTURE |
|
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molar Volume Vm | mL mol-1 | 140.0 | |
| Density ρ | g mL-1 | 1.05 | |
| Solubility Parameter δ | MPa1/2 | 19.3 - 19.8 | 19.6 |
| Molar Cohesive Energy Ecoh | J mol-1 | 52100 - 54900 | 53900 |
| Glass Transition Temperature Tg | K | 331 | |
| Molar Heat Capacity Cp | J (mol K)-1 | ||
| Entanglement Molecular Weight Me | g mol-1 | ||
| Index of Refraction n | none |
| PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
| Molecular Weight of Repeat unit | g mol-1 | 147.15 | |
| Van-der-Waals Volume VvW | mL mol-1 | 89.16 | |
| Molar Volume Vm | mL mol-1 | 129.6 - 136.8 | 134.2 |
| Density ρ | g mL-1 | 1.08 - 1.14 | 1.10 |
| Solubility Parameter δ | MPa1/2 | 20.7 - 21.1 | 21.0 |
| Molar Cohesive Energy Ecoh | J mol-1 | 57700 - 61200 | 59000 |
| Glass Transition Temperature Tg | K | 334 | |
| Molar Heat Capacity Cp | J (mol K)-1 | 187 - 200 | 193 |
| Entanglement Molecular Weight Me | g mol-1 | 63000 | |
| Index of Refraction n | none | 1.58 - 1.59 | 1.58 |