POLYMER CLASS | Epoxy or Phenoxy Rersin1 |
COMMON NAMES | Bisphenol-A diglycidyl ether epoxy or phenoxy resin, Poly(Bisphenol A-co-epichlorohydrin) |
STRUCTURE BASED NAME | Poly[1oxy-2-hydroxytrimethyleneoxy-1,4-phenylene(dimethylmethylene)-1,4-phenylene] |
ACRONYMS | Epoxy, Phenoxy |
CAS # | |
CurlySMILES | C{-}C(O)COc1ccc(cc1)C(C)(C)c2ccc(cc2)O(n+} |
CAS # | 201-245-8, 106-89-8 |
COMMON NAMES | Bisphenol A, Epichlorohydrin |
SMILES | CC(C)(c1ccc(cc1)O)c2ccc(cc2)O.C1C(O1)CCl |
Std. InChI | 1S/C15H16O2/c1-15(2,11-3-7-13(16)8-4-11)12-5-9-14(17)10-6-12/h3-10,16-17H,1-2H3.1S/C3H5ClO/c4-1-3-2-5-3/h3H,1-2H2 |
Std. InChIKey | IISBACLAFKSPIT-UHFFFAOYSA-N.BRLQWZUYTZBJKN-UHFFFAOYSA-N |
STRUCTURE |
![]() |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molar Volume Vm | mL mol-1 | 239 - 245 | 242 |
Density ρ | g mL-1 | 1.16 - 1.19 | 1.18 |
Solubility Parameter δ | MPa1/2 | 17.0 - 27.0 | 22.1 |
Molar Cohesive Energy Ecoh | J mol-1 | 72700 - 183400 | 123000 |
Glass Transition Temperature Tg | K | 371 - 373 | 372 |
Molar Heat Capacity Cp | J (mol K)-1 | ||
Entanglement Molecular Weight Me | g mol-1 | 1400 - 1900 | 1600 |
Index of Refraction n | none | 1.55 - 1.60 | 1.598 |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molecular Weight of Repeat unit | g mol-1 | 284.36 | |
Van-der-Waals Volume VvW | mL mol-1 | 159.34 | |
Molar Volume Vm | mL mol-1 | 249.7 - 253.0 | 251.6 |
Density ρ | g mL-1 | 1.12 - 1.14 | 1.13 |
Solubility Parameter δ | MPa1/2 | 21.0 - 21.6 | 21.2 |
Molar Cohesive Energy Ecoh | J mol-1 | 110500 - 117200 | 112700 |
Glass Transition Temperature Tg | K | 369 - 392 | 381 |
Molar Heat Capacity Cp | J (mol K)-1 | 339 - 358 | 346 |
Entanglement Molecular Weight Me | g mol-1 | 1400 - 1700 | 1500 |
Index of Refraction n | none | 1.55 - 1.64 | 1.58 |
1The reaction of bisphenol A with an excess amount of epichlorohydrin yields epoxies whereas an excess
amount of bisphenol A yields phenoxy resins.
Last updated: January 23, 2018