POLYMER CLASS | Polyesters |
COMMON NAMES | Poly(ethylene succinate) |
STRUCTURE BASED NAME | Poly(oxyethyleneoxybutanedioyl), Poly(oxyethyleneoxysuccinyl) |
ACRONYMS | |
CAS # | 25569-53-3 |
CurlySMILES | O{-}CCOC(=O)CCC{n+}(=O) |
CAS # | 203-740-4, 107-21-1 |
COMMON NAMES | Succinic acid, Ethanediol |
SMILES | OC(=O)CCC(=O)O.OCCO |
Std. InChI | 1S/C4H6O4/c5-3(6)1-2-4(7)8/h1-2H2,(H,5,6)(H,7,8).InChI=1S/C2H6O2/c3-1-2-4/h3-4H,1-2H2. |
Std. InChIKey | KDYFGRWQOYBRFD-UHFFFAOYSA-N.LYCAIKOWRPUZTN-UHFFFAOYSA-N |
STRUCTURE |
![]() |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molar Volume Vm | mL mol-1 | ||
Density ρ | g mL-1 | ||
Solubility Parameter δ | MPa1/2 | ||
Molar Cohesive Energy Ecoh | J mol-1 | ||
Glass Transition Temperature Tg | K | 262 - 272 | 267 |
Molar Heat Capacity Cp | J (mol K)-1 | ||
Entanglement Molecular Weight Me | g mol-1 | ||
Index of Refraction n | none | 1.47 - 1.48 | 1.47 |
PROPERTY | UNIT | VALUE / RANGE | PREFERRED |
Molecular Weight of Repeat unit | g mol-1 | 144.13 | |
Van-der-Waals Volume VvW | mL mol-1 | 71.3 | |
Molar Volume Vm | mL mol-1 | 102 - 110 | 106 |
Density ρ | g mL-1 | 1.31 - 1.41 | 1.36 |
Solubility Parameter δ | MPa1/2 | 20.6 - 22.0 | 21.4 |
Molar Cohesive Energy Ecoh | J mol-1 | 43400 - 53100 | 48700 |
Glass Transition Temperature Tg | K | 248 - 276 | 267 |
Molar Heat Capacity Cp | J (mol K)-1 | 252 - 263 | 256 |
Entanglement Molecular Weight Me | g mol-1 | 2190 - 2820 | 2430 |
Index of Refraction n | none | 1.47 - 1.50 | 1.48 |
Last updated: July 29, 2016