| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 199 - 204 |
| Density | g mL-1 | 1.30 - 1.48 |
| Coefficient of Thermal Expansion | cm / (cm °C) | 4.5 -7.0 |
| Heat Deflection Temperature, 0.5 MPa | °C | 68.9 - 77.2 |
| Heat Deflection Temperature, 1.8 MPa | °C | 67.2 - 77.2 |
| Thermal Conductivity x 10-5 | W / mK | 0.15 - 0.16 |
| Rockwell Hardness, A Scale (Shore D) | n/a | A50 - A95 (D81 - D86) |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 37.9 - 54.8 |
| Tensile Strength, Break at 23 C | MPa | |
| Elongation, Yield | % | |
| Elongation, Break | % | 25 - 58 |
| Tensile Modulus at 23 C | MPa | 2450 - 4700 |
| Flexural Strength, Yield | MPa | 73.1 - 95.1 |
| Flexural Modulus | MPa | 2500 - 4500 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | 35 - 80 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm x 1014 | 2.0 | |
| Dielectric Strength | V/mm x 104 | 1.4 - 2.0 | |
| Dielectric Constant @ 1 MHz | n/a | 2.7 - 3.9 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.02 - 0.022 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 160 - 188 | |
| Mold Shrinkage | % | 0.002 - 0.005 | |
| Continuous Service Temperature | °C | 55 - 60 | |
| Water Absorption, 24 hr. Immersion | % | 0.03 |