PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 327 - 346 |
Density | g mL-1 | 1.80 - 2.41 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 9.6 - 9.9 |
Heat Deflection Temperature, 0.5 MPa | °C | |
Heat Deflection Temperature, 1.8 MPa | °C | |
Thermal Conductivity | W / mK | 0.1 - 0.92 |
Shore Hardness, D Scale | n/a | D55 - D70 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 12.4 - 13.7 |
Tensile Strength, Break at 23 C | MPa | 26 - 35 |
Elongation, Yield | % | 325 |
Elongation, Break | % | 250 - 580 |
Tensile Modulus at 23 C | MPa | 480 - 630 |
Flexural Strength, Yield | MPa | |
Flexural Modulus | MPa | 490 |
Compressive Strength | MPa | |
Izod Notched | J / m | |
Izod Unnotched | J / m | 185 |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
Dielectric Strength | V/mm x 104 | 6 - 7 | |
Dielectric Constant @ 1 MHz | n/a | 2.02 - 2.1 | |
Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.3 - 0.7 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
Mold Shrinkage | % | ||
Continuous Service Temperature | °C | 260 | |
Water Absorption, 24 hr. Immersion | % | 0 - 0.02 |