| PROPERTY | UNIT | VALUE / RANGE |
| Melt Temperature | °C | 180 - 270 |
| Density | g mL-1 | 1.03 - 1.08 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 8 - 10 |
| Heat Deflection Temperature, 0.5 MPa | °C | 87 - 93 |
| Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | 75 - 91 |
| Thermal Conductivity | W / mK | 0.16 - 0.22 |
| Rockwell Hardness, L Scale (M Scale) | n/a | |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 20 - 28 |
| Tensile Strength, Break at 23 C | MPa | |
| Elongation, Yield | % | 1.2 |
| Elongation, Break | % | 10 - 55 |
| Tensile Modulus at 23 C | MPa | 1800 - 2280 |
| Flexural Strength, Yield | MPa | 25 - 43 |
| Flexural Modulus | MPa | 1900 - 2300 |
| Compressive Strength | MPa | |
| Izod Notched | J/m (kJ/m2) | 82 - 140 |
| Izod Unnotched | J/m | 744 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 1.8 | |
| Dielectric Constant @ 1 MHz | n/a | ||
| Dissipation Factor @ 1 MHz | n/a |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Linear Mold Shrinkage | cm/cm | ||
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.08 - 0.13 |