PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 180 - 260 |
Density | g mL-1 | 1.04 - 1.05 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 9.0 - 12.6 |
Heat Deflection Temperature, 0.5 MPa | °C | 77 - 97 |
Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | 78 - 98 |
Thermal Conductivity | W / mK | 0.35 |
Rockwell Hardness, M Scale | n/a | 71 - 80 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 44 - 52.4 |
Tensile Strength, Break at 23 C | MPa | 47 |
Elongation, Yield | % | 2.0 - 3.0 |
Elongation, Break | % | |
Tensile Modulus at 23 C | MPa | 3100 - 3170 |
Flexural Strength, Yield | MPa | 62 - 100 |
Flexural Modulus | MPa | 2900 - 3480 |
Compressive Strength | MPa | |
Izod Notched | J/m (kJ/m2) | 16 - 21 |
Izod Unnotched | J/m |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | > 6 x 1015 | |
Dielectric Strength | V/mm x 104 | 2.1 - 3.5 | |
Dielectric Constant @ 1 MHz | n/a | 2.20 - 2.35 | |
Dissipation Factor @ 1 MHz | n/a | 0.0001 - 0.0005 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | 170 - 240 | |
Linear Mold Shrinkage | cm/cm | 0.017 | |
Continuous Service Temperature | °C | -73 - 82 | |
Water Absorption, 24 hr. Immersion | % | > 0.01 |