| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | n.a. |
| Density | g mL-1 | 1.02 - 1.11 |
| Coefficient of Thermal Expansion | cm / (cm °C) x 10-5 | 5.2- 8.0 |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity | W / mK | 0.21 - 0.22 |
| Rockwell Hardness, A Scale (Shore D) | n/a | R115 - R120 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 67 |
| Tensile Strength, Break at 23 C | MPa | 65 |
| Elongation, Yield | % | 4 |
| Elongation, Break | % | 8 |
| Tensile Modulus at 23 C | MPa | 2400 |
| Flexural Strength, Yield | MPa | 95 |
| Flexural Modulus | MPa | 2400 |
| Compressive Strength, 1% - 2% | MPa | 17 - 30 |
| Charpy Impact Strength | kJ/m2 | 70 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm x 1014 | ||
| Dielectric Strength | V/mm x 104 | 1.6 - 2.4 | |
| Dielectric Constant @ 1 MHz | n/a | 2.0 - 2.8 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 7.0 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 230 - 300 | |
| Mold Shrinkage | % | 0.004 - 0.009 | |
| Continuous Service Temperature | °C | 95 | |
| Water Absorption, 24 hr. Immersion | % | 0.02 - 0.04 |