| PROPERTY | UNIT | VALUE / RANGE |
| Decomposition Temperature | °C | 250 |
| Density | g mL-1 | 1.26 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | |
| Heat Deflection Temperature, 0.5 MPa | °C | |
| Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | |
| Thermal Conductivity | W / mK | |
| Shore Hardness, D Scale | n/a | 74 - 79 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 4500 |
| Tensile Strength, Break at 23 C | MPa | 1,760 |
| Elongation, Yield | % | 3.0 |
| Elongation, Break | % | 150 |
| Tensile Modulus at 23 C | MPa | 2070 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | |
| Compressive Strength | MPa | |
| Izod Notched | J/m (kJ/m2) | 16 - 32 |
| Izod Unnotched | J/m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | ||
| Dielectric Constant @ 1 MHz | n/a | 3.0 | |
| Dissipation Factor @ 1 MHz | n/a |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
| Linear Mold Shrinkage | cm/cm | ||
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.4 |