PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 160 - 163 |
Density | g mL-1 | 0.90 - 0.91 (0.905) |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 8.0 - 10 |
Heat Deflection Temperature, 0.5 MPa | °C | 78 - 122 |
Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | |
Thermal Conductivity | W / mK | 0.17 - 0.23 |
Rockwell Hardness, R Scale | n/a | R65 - R110 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 31 - 45 |
Tensile Strength, Break at 23 C | MPa | 18 - 22 |
Elongation, Yield | % | 10 - 12 |
Elongation, Break | % | 50 - 145 |
Tensile Modulus at 23 C | MPa | 1950 |
Flexural Strength, Yield | MPa | |
Flexural Modulus | MPa | 1350 - 1800 |
Compressive Strength | MPa | |
Izod Notched | J/m (kJ/m2) | 35 - 60 (3.0 - 6.5) |
Izod Unnotched | J/m |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | > 1016 | |
Dielectric Strength | V/mm x 104 | 2.3 - 2.5 | |
Dielectric Constant @ 1 MHz | n/a | 2.1 - 2.6 | |
Dissipation Factor @ 1 MHz | n/a | 0.0002 - 0.0005 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | 200 - 280 | |
Linear Mold Shrinkage | cm/cm | 0.01 - 0.02 | |
Continuous Service Temperature | °C | 90 - 120 | |
Water Absorption, 24 hr. Immersion | % | 0.01 - 0.03 |