| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | |
| Density | g mL-1 | 1.16 - 1.18 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 7.25 - 9.50 |
| Heat Deflection Temperature, 0.5 MPa | °C | 79 - 85 |
| Heat Deflection Temperature, 1.8 MPa | °C | |
| Thermal Conductivity | W / mK | 0.19 - 0.23 |
| Rockwell Hardness, M Scale | n/a | M39 - M84 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | |
| Tensile Strength, Break at 23 C | MPa | 37 - 48 |
| Elongation, Yield | % | |
| Elongation, Break | % | 4.8 - 7.6 |
| Tensile Modulus at 23 C | MPa | 1725 - 2790 |
| Flexural Strength, Yield | MPa | 71 - 99 |
| Flexural Modulus | MPa | 1860 - 2620 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | 32 - 59 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 1.0 - 3.1 | |
| Dielectric Constant @ 1 MHz | n/a | 2.2 - 3.9 (2.8) | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 0.025 - 0.046 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 121 - 157 | |
| Mold Shrinkage | % | ||
| Continuous Service Temperature | °C | 71 - 85 | |
| Water Absorption, 24 hr. Immersion | % | 0.3 - 0.5 |