| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | |
| Density | g mL-1 | 1.47 - 1.52 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 0.20- 0.60 |
| Heat Deflection Temperature, 0.5 MPa | °C | 144 - |
| Heat Deflection Temperature, 1.8 MPa | °C | 140 - |
| Thermal Conductivity | W / mK | |
| Shore Hardness, R & M Scale | n/a | |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 113 |
| Tensile Strength, Break at 23 C | MPa | 110 - 115 |
| Elongation, Yield | % | |
| Elongation, Break | % | 1.8 |
| Tensile Modulus at 23 C | MPa | 9400 - 12000 |
| Flexural Strength, Yield | MPa | |
| Flexural Modulus | MPa | 8600 |
| Compressive Strength | MPa | |
| Izod Notched | kJ / m2 | 8 |
| Izod Unnotched | kJ / m2 |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 3.6 | |
| Dielectric Constant @ 1 MHz | n/a | 3.2 - 3.5 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 300 | |
| Linear Mold Shrinkage | cm/cm | ||
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.24 |