| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | 310 - 330 |
| Density | g mL-1 | 1.19 - 1.22 |
| Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 6.2 - 7.0 |
| Heat Deflection Temperature, 0.5 MPa | °C | 137 - 146 |
| Heat Deflection Temperature, 1.8 MPa annealed (unannealed) | °C | 135 - 141 (123 - 132) |
| Thermal Conductivity | W / mK | 0.19 - 0.20 |
| Shore Hardness, R Scale (M Scale) | n/a | R118 - 123 (M59 - M70) |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 61 - 67 |
| Tensile Strength, Break at 23 C | MPa | 55 - 72 |
| Elongation, Yield | % | 6 - 6.2 |
| Elongation, Break | % | 120 - 150 |
| Tensile Modulus at 23 C | MPa | 2350 - 2400 |
| Flexural Strength, Yield | MPa | 90 - 92 |
| Flexural Modulus | MPa | 2235 - 2500 |
| Compressive Strength | MPa | |
| Izod Notched | J/m (kJ/m2) | 650 - 900 (65 - 90) |
| Izod Unnotched | J/m | No Break |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | > 2.0 x 1017 | |
| Dielectric Strength | V/mm x 104 | 1.5 - 3.4 | |
| Dielectric Constant @ 1 MHz | n/a | 2.95 - 3.00 | |
| Dissipation Factor @ 1 MHz | n/a | 0.002 - 0.01 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 280 - 300 | |
| Linear Mold Shrinkage | cm/cm | 0.003 - 0.007 | |
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.15 - 0.30 |