PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 163 - 165 |
Density | g mL-1 | 0.89 - 0.91 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | |
Heat Deflection Temperature, 0.5 MPa | °C | 80 - 120 |
Heat Deflection Temperature, 1.8 MPa (unannealed) | °C | 51 - 86 |
Thermal Conductivity | W / mK | |
Rockwell Hardness, R Scale | n/a | 86 - 105 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 17 - 31 |
Tensile Strength, Break at 23 C | MPa | 15 - 19 |
Elongation, Yield | % | 5 - 15 |
Elongation, Break | % | 130 - 550 |
Tensile Modulus at 23 C | MPa | 1100 - 1400 |
Flexural Strength, Yield | MPa | |
Flexural Modulus | MPa | 950 - 1200 |
Compressive Strength | MPa | |
Izod Notched | kJ/m2 | 15 - 50 |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
Dielectric Strength | V/mm x 104 | ||
Dielectric Constant @ 1 MHz | n/a | ||
Dissipation Factor @ 1 MHz | n/a |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
Linear Mold Shrinkage | cm/cm | ||
Continuous Service Temperature | °C | ||
Water Absorption, 24 hr. Immersion | % |