PROPERTY | UNIT | VALUE / RANGE |
Melting Point | °C | 126 - 135 |
Density | g mL-1 | 0.955 - 0.961 |
Coefficient of Thermal Expansion x 10-5 | cm / (cm °C) | 12.5 - 18.0 |
Heat Deflection Temperature, 0.5 MPa | °C | 64 - 77 |
Heat Deflection Temperature, 1.8 MPa (unannealed) | °C | 76.5 - 78 |
Thermal Conductivity | W / mK | 0.35 - 0.49 |
Shore Hardness, D Scale | n/a | 55 - 67 |
PROPERTY | UNIT | VALUE / RANGE |
Tensile Strength, Yield at 23 C | MPa | 23.0 - 29.5 |
Tensile Strength, Break at 23 C | MPa | 30.5 - 33 |
Elongation, Yield | % | 9 - 18 |
Elongation, Break | % | 600 - 1350 |
Tensile Modulus at 23 C | MPa | 900 - 1550 |
Flexural Strength, Yield | MPa | |
Flexural Modulus | MPa | 970- 1380 |
Compressive Strength | MPa | |
Izod Notched | J/m (kJ/m2) | 71 - 159 (20) |
Izod Unnotched | J/m | No Break |
PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | 6 x 1015 | |
Dielectric Strength | V/mm x 104 | 2.1 - 3.5 | |
Dielectric Constant @ 1 MHz | n/a | 2.2 - 2.4 | |
Dissipation Factor @ 1 MHz | n/a | 0.0001 - 0.0005 |
PROPERTY | UNIT | VALUE / RANGE | |
| °C | ||
Linear Mold Shrinkage | cm/cm | 0.017 | |
Continuous Service Temperature | °C | -73 - 82 | |
Water Absorption, 24 hr. Immersion | % | 0.01 - 0.03 |