| PROPERTY | UNIT | VALUE / RANGE |
| Melting Point | °C | - |
| Density | g mL-1 | 1.03 - 1.14 |
| Coefficient of Thermal Expansion | cm / (cm °C) | 2.0 - 10.3 |
| Heat Deflection Temperature, 0.5 MPa | °C | 88 - 107 |
| Heat Deflection Temperature, 1.8 MPa | °C | 71 - 103 |
| Thermal Conductivity x 10-5 | W / mK | 0.17 - 0.23 |
| Rockwell Hardness, R Scale | n/a | R102 - R104 |
| PROPERTY | UNIT | VALUE / RANGE |
| Tensile Strength, Yield at 23 C | MPa | 28 - 120 |
| Tensile Strength, Break at 23 C | MPa | |
| Elongation, Yield | % | 1.0 - 50 |
| Elongation, Break | % | 2.5 - 40 |
| Tensile Modulus at 23 C | MPa | 420 - 2500 |
| Flexural Strength, Yield | MPa | 50 - 162 |
| Flexural Modulus | MPa | 1550 - 2580 |
| Compressive Strength | MPa | |
| Izod Notched | J / m | 72 |
| Izod Unnotched | J / m |
| PROPERTY | UNIT | VALUE / RANGE | |
| Ohm-cm | ||
| Dielectric Strength | V/mm x 104 | 1.4 - 3.1 | |
| Dielectric Constant @ 1 MHz | n/a | 3.1 - 3.4 | |
| Dissipation Factor @ 1 MHz | n/a, x 10-4 | 80 - 90 |
| PROPERTY | UNIT | VALUE / RANGE | |
| °C | 205 - 275 | |
| Mold Shrinkage | % | 0.002 - 0.007 | |
| Continuous Service Temperature | °C | ||
| Water Absorption, 24 hr. Immersion | % | 0.26 - 1.70 |